A diamond-like carbon thin film was deposited on the outer face of the germanium (Ge) window to protect the infrared lenses from a harsh environment in automotive application. Infrared transmittance and residual stress of a tetrahedral amorphous carbon (ta-C) thin film by a filtered cathodic vacuum arc (FCVA) source were investigated to increase the lifetime of a Ge window. They were found to have a trade-off relation about the change of the substrate pulse voltage. By introducing methane gas in FCVA deposition process, a hydrogenated ta-C (ta-C:H) thin film of which both IR transmittance and residual stress was improved could be obtained. A Ge window coated with ta-C:H thin film with 1.43 μm thickness showed anti-reflective effect in long-wave infrared. The hardness of ta-C:H thin film on Ge window was higher than 30 GPa. Adhesion, severe abrasion, temperature, humidity and salt solubility tests were carried out in accordance with MIL-C-48497A.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.