Degradation of ZnO-based window layers for thin-film CIGS by accelerated stress exposures

F. J. Pern; R. Noufi; B. To; C. DeHart; X. Li; S. H. Glick

doi:10.1117/12.795097

10 September 2008 Degradation of ZnO-based window layers for thin-film CIGS by accelerated stress exposures

F. J. Pern, R. Noufi, B. To, C. DeHart, X. Li, S. H. Glick

Proceedings Volume 7048, Reliability of Photovoltaic Cells, Modules, Components, and Systems; 70480P (2008) https://doi.org/10.1117/12.795097
Event: Solar Energy + Applications, 2008, San Diego, California, United States

Abstract

The reliability of ZnO-based window layer for CuInGaSe₂ (CIGS) solar cells was investigated. Samples of RF magnetron-sputtered, single-layer intrinsic and Al-doped ZnO and their combined bilayer on glass substrates were exposed in a weatherometer (WOM) and damp heat (DH) conditions with or without acetic acid vapor. Some preliminary samples of single-layer Al-doped Zn_1-xMg_xO (ZMO) alloy, a potential replacement for Al:ZnO with a wider bandgap, were also evaluated in the DH. The Al-doped ZnO and ZMO films showed irreversible loss in the conducting properties, free carrier mobility, and characteristic absorption band feature after <500-h DH exposure, with the originally clear transparent films turned into white hazy insulating films and the degradation rate follows the trend of (DH + acetic acid) > DH > WOM. The degradation rate was also reduced by higher film thickness, higher deposition substrate temperature, and dry-out intervals. The results of X-ray diffraction analysis indicate that the ZnO-based films underwent structural degeneration by losing their highly (002) preferential orientation with possible transformation from hexagonal into cubic and formation of Zn(OH)₂. Periodic optical micro-imaging observations suggested a temporal process that involves initial hydrolysis of the oxides at sporadic weak spots, swelling and popping of the hydrolyzed spots due to volume increase, segregation of hydrolyzed regions causing discontinuity of electrical path, hydrolysis of the oxide-glass interface, and finally, formation of insulating oxides/hydroxides with visible delamination over larger areas.

Citation Download Citation

F. J. Pern, R. Noufi, B. To, C. DeHart, X. Li, and S. H. Glick "Degradation of ZnO-based window layers for thin-film CIGS by accelerated stress exposures", Proc. SPIE 7048, Reliability of Photovoltaic Cells, Modules, Components, and Systems, 70480P (10 September 2008); https://doi.org/10.1117/12.795097

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available