Impedance based corrosion detection

Garnett E. Simmers Jr.; Henry A. Sodano; Gyuhae Park; Daniel J. Inman

doi:10.1117/12.599780

19 May 2005 Impedance based corrosion detection

Garnett E. Simmers Jr., Henry A. Sodano, Gyuhae Park, Daniel J. Inman

Proceedings Volume 5767, Nondestructive Evaluation and Health Monitoring of Aerospace Materials, Composites, and Civil Infrastructure IV; (2005) https://doi.org/10.1117/12.599780
Event: Nondestructive Evaluation for Health Monitoring and Diagnostics, 2005, San Diego, CA, United States

Abstract

Corrosion begins as moisture penetrates the protective barrier of a surface, starting an electrochemical process which over time leads to surface pitting. The combined action of mechanical stresses and corrosion induced pitting reduces structural integrity as the pits enlarge to form nucleation sites for surface cracks, which propagate into through-the-thickness cracks. In most cases, the total mass loss due to corrosion within the structure is small; however, significant reductions in mechanical strength and fatigue life can occur in the corroded material leading to advanced crack growth rates or fast fracture. Since the structural damage due to localized corrosion pitting is small and the crack growth rates may be large, traditional inspections methods and "find it and fix it" maintenance approaches may lead to catastrophic mechanical failures. Therefore, precise structural health monitoring of pre-crack surface corrosion is paramount to understanding and predicting the effect corrosion has on the fatigue life and integrity of a structure. In this study, the impedance method was experimentally tested to detect and quantify the onset and growth of pre-crack surface corrosion in beam and plate like structures. Experimental results indicate the method is an effective detection and tracking tool for corrosion induced structural damage in plates and beams. Additionally, impedance based monitoring of the corrosive effect on the piezoelectric sensors may serve as a useful tool for predicting corrosion growth rates on the surface of structures.

Citation Download Citation

Garnett E. Simmers Jr., Henry A. Sodano, Gyuhae Park, and Daniel J. Inman "Impedance based corrosion detection", Proc. SPIE 5767, Nondestructive Evaluation and Health Monitoring of Aerospace Materials, Composites, and Civil Infrastructure IV, (19 May 2005); https://doi.org/10.1117/12.599780

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available