26 March 1998 Image formation properties of As40S20Se40 thin layers
Alexander V. Stronski, Miroslav Vlcek, A. Sklenar, Peter E. Shepeljavi, Pavel F. Oleksenko, Tomas Wagner
Author Affiliations +
Proceedings Volume 3294, Holographic Materials IV; (1998) https://doi.org/10.1117/12.304529
Event: Photonics West '98 Electronic Imaging, 1998, San Jose, CA, United States
Abstract
The present paper is concerned with investigations of image formation properties of As40S20Se40 thin layers. Spectral dependence of the refraction index n of variously treated samples was estimated from optical transmission in the spectral region 400-2500 nm. The n energy dependence of variously treated samples was fitted by the Wemple- DiDomenico dispersion relationship and used to estimate the single-oscillator model parameters. It was found, that exposure, as well as annealing leads to the increase in n values over the all investigated spectral region. Changes of the parameters of the single-oscillator model induced by treatment are discussed on the base of photo- and thermally- induced structural changes, which were directly confirmed by Raman scattering measurements. Such photoinduced structural changes provide good etching selectivity of As40S20Se40 layers in nonaqueous amine based solvents. The best obtained sensitivity values consisted of approximately 40 cm2/J. Surface relief patterns that were fabricated have good surface quality.Diffraction efficiency values of holographic diffraction gratings obtained on the base of As40S20Se40 layers consisted of 60-70 percent.
© (1998) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Alexander V. Stronski, Miroslav Vlcek, A. Sklenar, Peter E. Shepeljavi, Pavel F. Oleksenko, and Tomas Wagner "Image formation properties of As40S20Se40 thin layers", Proc. SPIE 3294, Holographic Materials IV, (26 March 1998); https://doi.org/10.1117/12.304529
Lens.org Logo
CITATIONS
Cited by 1 scholarly publication.
Advertisement
Advertisement
RIGHTS & PERMISSIONS
Get copyright permission  Get copyright permission on Copyright Marketplace
KEYWORDS
Image acquisition

Thin films

Annealing

Glasses

Raman spectroscopy

Statistical analysis

Transmittance

RELATED CONTENT


Back to Top