Damage free Al doping on 4H-SiC with passivation films using XeF excimer laser irradiation in AlCl3 acid solution

T. Tsuchiya; A. Suwa; A. Ikeda; D. Nakamura; T. Asano; H. Ikenoue

doi:10.1117/12.2250712

20 February 2017 Damage free Al doping of 4H-SiC with passivation films using XeF excimer laser irradiation in AlCl₃ acid solution

T. Tsuchiya, A. Suwa, A. Ikeda, D. Nakamura, T. Asano, H. Ikenoue

Author Affiliations +

Proceedings Volume 10091, Laser Applications in Microelectronic and Optoelectronic Manufacturing (LAMOM) XXII; 1009106 (2017) https://doi.org/10.1117/12.2250712
Event: SPIE LASE, 2017, San Francisco, California, United States

Abstract

We propose an innovative method for aluminum doping of 4H-SiC with passivation films, induced by XeF excimer laser irradiation in AlCl3 aqueous solution (28.6 wt%). A 100-nm thick Si passivation film was deposited on an n-type 4H-SiC substrate by physical vapor deposition. Using a laser beam (200 μm × 170 μm) with an irradiation fluence of 0.5–5.0 J/cm², 1–300 shots were administered. After laser irradiation of 1.0 J/cm² and 300 shots, an Al-Si-O compound film was formed on the SiC surface. The compound film was removed by chemical wet etching and plasma treatment. After the removal of the compound film, no irradiation damage was observed on the SiC surface. From the results of secondary ion mass spectrometry measurements, high concentration aluminum doping (about 1 × 10²⁰ /cm³ at the surface) was confirmed. The I-V characteristics of the junction between the n-type substrate and the irradiation area indicated clear rectification with a large on/off ratio of 9 decades in the range of ±10 V. When forward biased, electroluminescence phenomenon with a peak at 387 nm, corresponding to the electroluminescence of SiC’s band gap, was confirmed. These results prove the achievement of Al doping of n-type SiC to p-type using laser irradiation without any damage to the SiC surface.

Conference Presentation

Citation Download Citation

T. Tsuchiya, A. Suwa, A. Ikeda, D. Nakamura, T. Asano, and H. Ikenoue "Damage free Al doping of 4H-SiC with passivation films using XeF excimer laser irradiation in AlCl₃ acid solution", Proc. SPIE 10091, Laser Applications in Microelectronic and Optoelectronic Manufacturing (LAMOM) XXII, 1009106 (20 February 2017); https://doi.org/10.1117/12.2250712

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available